The rule of optimization based on film performance meeting the agronomic requirement to reduce energy consumption and save raw materials as much as possible was applied to determine the optimum combination of the factors. The result was that when rosin was held at 0.8%, bauxite was held at 4%, wet strength agent was held at 1.8%, beating degree was held at 35 SR°, grammage was held at 80 g/m2, the performance that was dry tensile strength was greater than 30N, wet tensile strength was greater than 12N, the degradation period was 35 days to 60 days could be obtained, seeing in Fig 3-13.

3.5 Manufacturing technology

Based on the above research results, manufacturing technology of the biogas residue fibre film was obtained, seeing Fig 3-14.